A200 ABS like Resin is a white, tough resin, suitable for SLA printer with355nm laser light sources. The printed products have the toughness and strength similar to those of ABS materials, and can exc
Details
Product Feature
White, tough resin, suitable for SLA printer with355nm laser light sources. The printed products have the toughness and strength similar to those of ABS materials, and can excellently display the details of the manufacturing process.
Product Application
Can be used to produce master molds for consumer electronics, electrical components, chassis, automobiles, medical and other industrial fields. It can also be used for the creation of concept models and functional components, and is applicable in fields such as education.
TYPICAL UNCURED PROPERTIES | |
Chemical Type | Acrylate/Epoxy resin |
Appearance | White |
Density ，g/cm³@25℃ | 1.11 ~ 1.18 |
Viscosity ，cps@25℃,100rpm | 300 ~ 480 |
CURING GUIDELINES | |
Curing Method | UV Curing |
Wavelength ，nm | 355 |
Ec ，mJ/cm² | 7.0 ~ 8.6 |
Dp ，mm | 0.130 ~ 0.150 |
Building Layer Thickness ，mm | 0.05 ~ 0.12 |
Using Temperature ，℃ | 20 ~ 28 |
TYPICAL CURED PROPERTIES | ||
MEASUREMENT | VALUE | TEST METHOD |
Density ，g/cm³ | 1.15~ 1.20 | ASTM D792 |
Tensile Modulus ，MPa | 2550 ~ 2700 | ASTM D638M |
Tensile Strength ，MPa | 45 ~ 58 | ASTM D638M |
Elongation At Break ，% | 8 ~ 12 | ASTM D638M |
Flexural Modulus ，MPa | 2650 ~ 2850 | ASTM D790M |
Flexural Strength ，MPa | 80 ~ 90 | ASTM D790M |
Izod Notch Impact Strength ，J/m | 28 ~ 35 | ASTM D256 |
Heat Deflection Temperature ，℃@0.46MPa | 56 ~ 65 | ASTM D648 |
Glass Transition Temperature ，℃ | 50 ~ 58 | ASTM E1545-00 |
Coefficient Of Thermal Expansion ，℃ | 90~103*E-6 | ASTM E831-05 |
Poisson’s Ratio | 0.39 ~ 0.43 | ASTM D638 |
Hardness ，Shore D | 82 ~ 86 | ASTM D2240 |
Water Abortion ，% | 0.46 | ASTM D570-98 |
Dielectric Constant 60Hz | 3.8 ~ 4.8 | ASTM D150-98 |
Dielectric Constant 1KHz | 3.2 ~ 4.2 | ASTM D150-98 |
Dielectric Constant 1MHz | 3.0 ~ 4.0 | ASTM D150-98 |
Dielectric Strength kV/mm | 12.5 ~ 16.0 | ASTM D149-97A |